Hoʻohana: Hoʻohana nui ʻia i ka mīkini brushless, ka mīkini ʻenehana paʻa paʻa, ka mīkini lole, kaʻa kaʻa, ka mīkini paʻa paʻa pololei, ka moki laina, ka ʻenekini hoʻoheheʻe ea, ka mīkini mīkini paʻa mau loa, ka mīkini kai, ka mea hoʻoheheʻe paʻa mau, ka mīkini hoʻokele mau loa. , ka mining paʻa kaʻa kaʻa, ka hui pū ʻana, ka ʻenekini paʻa mau loa, ke kaʻa kaʻa no ka EV, ka mīkini pahū, ke kaʻa EPS, ka ʻike a me nā wahi ʻē aʻe.
Hoʻopilikino ʻia ka huahana: hoʻopili ʻia ka magnet, hiki ke lōʻihi mai 0.5mm-200mm, ākea mai 0.5mm-150mm, mānoanoa mai 0.5mm-70mm, hiki ke hoʻokō i ka koi o nā mea kūʻai aku.
Ka uhi ʻana: He maʻalahi ka oxidize NdfeB magnet, no laila pono ia i kahi uhi, ka uhi i hoʻohana mau ʻia ma ka mākeke e like me:
1. ZN plating (kahi ʻano o ka hoʻoheheʻe metala, hiki i ka hoʻāʻo ʻana o ka paʻakai paʻakai ke hōʻea i nā hola 24-48, ke kumu kūʻai kiʻekiʻe, no laila ʻo ia kekahi o nā koho maikaʻi loa no ka hapa nui o nā mea kūʻai aku).
2. NICUNI (kekahi 'ano o ka metala i uhi 'ia, ka pa'akai pa'akai ho'ā'o hiki i 48-72 hola, koina hana 'oi aku ka kiʻekiʻe ma mua o ZN, akā nō naʻe loa hoʻohana 'ia i loko o ka makeke i ka hui 'ana ua paʻakikī, nā huahana corrosion kū'ē koi o ka mea kūʻai mai hiki. koho).
3. Epoxy (ka uhi non-metallic, non-magnetic conductivity, hiki ke hōʻemi i ka nalowale o ka mīkini eddy i kēia manawa, hiki i ka hoʻāʻo paʻakai paʻakai ke hiki i nā hola 72-96, ʻoi aku ka nui o ke kumukūʻai ma mua o ka ZN a NICUNI coating.)
4. ʻO nā uhi ʻē aʻe i hoʻohana ʻia: Phosphate, Sn, Au, Ag, Parylene a pēlā aku ...
ʻO ka hoʻomanawanui: ʻO ka maʻamau ko mākou hoʻomanawanui magnet +/-0.05mm ma hope o ka uhi ʻana.
NdFeB Hana Hana
Hoʻolauna hoʻouhi
Ili | Ka uhi ʻana | Mānoanoa μm | kalakala | Nā hola SST | Nā hola PCT | |
Nikela | Ni | 10~20 | Kahinahinahinahina | >24~72 | >24~72 | |
Ni+Cu+Ni | ||||||
Nikela ʻeleʻele | Ni+Cu+Ni | 10~20 | ʻEleʻele ʻulaʻula | >48~96 | >48 | |
Cr3+Zink | Zn C-Zn | 5~8 | ʻO Brighe Blue Kala ʻulaʻula | >16~48 >36~72 | --- | |
Sn | Ni+Cu+Ni+Sn | 10~25 | Kālā kala | >36~72 | >48 | |
Au | Ni+Cu+Ni+Au | 10~15 | gula | >12 | >48 | |
Ag | Ni+Cu+Ni+Ag | 10~ 15 | Kālā kala | >12 | >48 | |
Epoxy | Epoxy | 10~20 | ʻEleʻele/Heleele | >48 | --- | |
Ni+Cu+Epoxy | 15~30 | >72~108 | --- | |||
Zn+Epoxy | 15~25 | >72~108 | --- | |||
Ka hoʻopaʻapaʻa | --- | 1~3 | Kahinahinahina | Palekana manawa | --- | |
Phosphate | --- | 1~3 | Kahinahinahina | Palekana no ka manawa) | --- |
Nā ʻano kino
'ikamu | Nā ʻāpana | Waiwai Kuhikuhi | Unite |
Mākēneki kōkua Waiwai | Hiki ke hoʻohuli i ka wela o Br | -0.08--0.12 | %/℃ |
Huli Ho'olele 'ana i ka wela o ka Hcj | -0.42~-0.70 | %/℃ | |
Wela Kūikawā | 0.502 | KJ·(Kg · ℃)-1 | |
Ka Mahana Curie | 310~380 | ℃ | |
Kino Mechanical Waiwai | ʻO ka mānoanoa | 7.5-7.80 | g/cm3 |
ʻO Vickers Paʻakikī | 650 | Hv | |
Kū'ē Uila | 1.4x10-6 | μQ ·m | |
Ka ikaika hoʻopili | 1050 | MPa | |
Ikaika U'i | 80 | Mpa | |
Kulou ikaika | 290 | Mpa | |
ʻO ka hoʻoili wela | 6~8.95 | W/m ·K | |
Opio Modulus | 160 | GPa | |
Hoʻonui wela(C⊥) | -1.5 | 10-6/℃-1 | |
Hoʻonui wela (CII) | 6.5 | 10-6/℃-1 |